dancerdark2000 发表于 2007-3-9 10:00:00

[原创]ENIG专贴

**** Hidden Message *****
[此贴子已经被作者于2007-5-31 16:30:55编辑过]

dancerdark2000 发表于 2007-3-9 10:02:00

孔环甩镍金图片

<br/>

dancerdark2000 发表于 2007-3-9 10:06:00

孔环铜面异常图片（铜板需特殊处理）

<br/>

dancerdark2000 发表于 2007-3-9 10:18:00

&nbsp;孔环铜面异常处EDS分析<p class="MsoNormal"><span style="FONT-FAMILY: PMingLiU; FONT-SIZE: 9pt; mso-bidi-font-size: 12.0pt; mso-ascii-font-family: &quot;Times New Roman&quot;; mso-hansi-font-family: &quot;Times New Roman&quot;; mso-fareast-language: ZH-CN;">谱图处理 : </span></p><p class="MsoNormal"><span style="FONT-FAMILY: PMingLiU; FONT-SIZE: 9pt; mso-bidi-font-size: 12.0pt; mso-ascii-font-family: 'Times New Roman'; mso-hansi-font-family: 'Times New Roman'; mso-fareast-language: ZH-CN;">元素&nbsp; 重量&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 原子&nbsp;<br/>&nbsp;&nbsp; &nbsp;&nbsp; 百分比&nbsp;&nbsp;&nbsp;&nbsp; 百分比&nbsp;<br/>C K&nbsp;&nbsp; 29.13&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 56.92&nbsp;<br/>O K &nbsp; 15.28&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 22.42&nbsp;<br/>Al K&nbsp;&nbsp; 0.56&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 0.49&nbsp;<br/>Si K &nbsp; 0.76&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 0.63&nbsp;<br/>S K&nbsp;&nbsp;&nbsp; 1.90&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 1.39&nbsp;<br/>Cu L &nbsp; 46.34&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 17.12&nbsp;<br/>Ba L&nbsp;&nbsp; 6.03&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 1.03&nbsp;<br/>&nbsp;&nbsp;&nbsp;<br/>总量&nbsp;100.00&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; EDS分析取点位置<img align="baseline" alt="" border="9" hspace="0" src="C:\Documents and Settings\陈光辉\桌面\复件 未命名1.bmp"/></span></p><p class="MsoNormal"><span lang="EN-US" style="FONT-SIZE: 9pt; mso-bidi-font-size: 12.0pt;"><p></p></span></p><p></p><p></p><p></p><p></p><p></p><p></p><p></p><p></p>
[此贴子已经被作者于2007-3-9 13:55:53编辑过]

dancerdark2000 发表于 2007-3-9 10:23:00

<p>孔环甩镍金处EDS分析</p><p>谱图处理 : </p><p>元素&nbsp; 重量&nbsp;&nbsp;&nbsp; 原子&nbsp;<br/>&nbsp;&nbsp; &nbsp;&nbsp; 百分比&nbsp;&nbsp;&nbsp; 百分比&nbsp;<br/>C K&nbsp;&nbsp; 46.64&nbsp;&nbsp;&nbsp;&nbsp; 70.42&nbsp;<br/>O K&nbsp;&nbsp; 15.76&nbsp;&nbsp;&nbsp;&nbsp; 17.87&nbsp;<br/>Si K&nbsp; 0.36&nbsp;&nbsp;&nbsp;&nbsp; 0.23&nbsp;<br/>P K&nbsp;&nbsp; 2.97&nbsp;&nbsp;&nbsp;&nbsp;&nbsp; 1.74&nbsp;<br/>Ni K&nbsp;&nbsp;&nbsp;27.91&nbsp;&nbsp;&nbsp;&nbsp; 8.62&nbsp;<br/>Cu L&nbsp; 1.81&nbsp;&nbsp;&nbsp;&nbsp; 0.52&nbsp;<br/>Ba L&nbsp; 4.56&nbsp;&nbsp;&nbsp;&nbsp; 0.60&nbsp;<br/>&nbsp;&nbsp;&nbsp;<br/>总量&nbsp;100.00&nbsp;&nbsp;</p><p>EDS取点位置<img align="baseline" alt="" border="9" hspace="0" src="C:\Documents and Settings\陈光辉\桌面\复件 未命名.bmp"/></p>
[此贴子已经被作者于2007-3-9 13:59:14编辑过]

dearlinge 发表于 2007-3-10 11:17:00

学习一下

jybenben 发表于 2007-3-12 10:34:00

dancerdark2000 发表于 2007-3-12 10:50:00

<p>金面发白问题:</p><p>由于化镍金金层较薄,金面发白往往是表现在金面,根源在镍面.多数时候镍层的结晶结构已经出现异常.而镍面异常的原因主要有两个方面:</p><p>1、镍层耐腐蚀性差，很容易被攻击；</p><p>2、金槽的攻击性过强，如温度控制过高，金浓度偏低等等，在槽液的前期和后期表现比较明显，上村TKK-51系列在新开缸做&gt;3u"的金板很明显。</p>
[此贴子已经被作者于2007-3-23 15:06:47编辑过]

dancerdark2000 发表于 2007-3-12 11:44:00

<br/>

dancerdark2000 发表于 2007-3-12 11:47:00

<p>&nbsp;手指金面发白处镍面结晶结构</p><br/>
[此贴子已经被作者于2007-3-12 11:48:20编辑过]